Honeywell ACLAR® Rx 160 CTFE Homopolymer, Barrier Film
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | Honeywell |
| Trade Name | ACLAR® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® Rx 160 CTFE Homopolymer, Barrier Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Aclar® Rx160 is a 0.60 mil (15 micron) PCTFE homopolymer, high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment and offers all the benefits of Aclar® where barrier considerations are less demanding.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.11 g/cc | 2.11 g/cc | ASTM D1505 |
| Density | 2.10 g/cc | 0.0760 lb/in³ | Yield Density |
| Water Vapor Transmission | 0.0510 g/m²/day | 0.00328 g/100 in²/day | 77°F (25°C) / 60%RH; ASTM F1249 |
| 0.0930 g/m²/day | 0.00599 g/100 in²/day | 86°F (30°C) / 60%RH; ASTM F1249 | |
| 0.0960 g/m²/day | 0.00618 g/100 in²/day | 86°F (30°C) / 65% RH; ASTM F1249 | |
| 0.330 g/m²/day | 0.0213 g/100 in²/day | 104°F (40°C) / 75%RH; ASTM F1249 | |
| 0.420 g/m²/day | 0.0270 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 | |
| Thickness | 15.2 microns | 0.600 mil | |
| Surface Tension | >= 42 dynes/cm | >= 42 dynes/cm | treated side; ASTM D882 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 80 - 130 % | 80 - 130 % | ASTM D882 |
| Film Elongation at Break, TD | 200 - 275 % | 200 - 275 % | ASTM D882 |
| Secant Modulus, MD | 1.379 - 1.655 GPa | 200.0 - 240.0 ksi | ASTM D882 |
| Secant Modulus, TD | 1.241 - 1.517 GPa | 180.0 - 220.0 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 75.8 - 117 MPa | 11000 - 17000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.9 - 48.3 MPa | 5500 - 7000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 211 °C | 412 °F | crystalline melting point; ASTM D4591 |
| Shrinkage, MD | <= 12 % | <= 12 % | 10 mins.@ 300°F/149°C; ASTM D1204 |
| Shrinkage, TD | <= -12.0 % | <= -12.0 % | 10 mins.@ 300°F/149°C; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJMF113L Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics Lexan® FXM141R PC
- Quadrant EPP Nylatron® MD PA 6 + metal detectable additive, extruded (ISO Data)
- DuPont Performance Polymers Zytel® 444AHS BK152 Nylon 66 (Unverified Data**)
- DSM Akulon® F223-DH (Dry) Low/Medium Viscosity, Heat Stabilized Nylon 6 (North America) (discontinued **)
- Techmer ES HiFill® PET GF45 X 45% Glass Filled
- Solvay SUPER CEROXâ„¢ 1663 Surfactant
- Wellman Wellamid® GS40-66 22L-Bk1 40% Glass Sphere Filled Nylon 66
- 3M Dyneon™ PFE 80Z Peroxide Cure Perfluoroelastomer
Copyright © lookpolymers.com All Rights Reserved