- NOVA Chemicals Sclair® 11L4B Octene LLDPE Film Resin (discontinued **)
NOVA Chemicals Sclair® 11L4B Octene LLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 11L4B Octene LLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, excellent seal characteristics.Applications: Specialty lamination, co-extrusion of food and liquid packaging.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.72 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 624 % | 624 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Secant Modulus, MD | 0.203 GPa | 29.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.210 GPa | 30.5 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.12 | >= 0.12 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 18.0 g/micron | 457 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.0 g/micron | 584 g/mil | ASTM D1922 |
| Dart Drop | 8.00 g/micron | 203 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 11 % @Thickness 0.0250 mm |
11 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 51 % | 51 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 220 °C | 410 - 428 °F |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CM100LN Polypropylene, Impact Copolymer, Medium Impact, Nucleated, Antistat, Injection Molding
- Resin Technology Group TIGA 901 Room Temperature Curing Silver Conductive Epoxy
- 3M Dyneon™ PVDF 6020/1001 Polyvinylidene Fluoride (discontinued **)
- Lord Adhesives Aeroglaze® 9744 Epoxy Primer/Tie-Coat
- LyondellBasell Alathon® L4907 High Density Polyethylene
- SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC (Asia Pacific)
- Bhansali Engineering Abstron PT-45M ABS Antistatic Extrusion Grade
- E-Polymers EFLEX® M300 HDPE
Copyright © lookpolymers.com All Rights Reserved