NOVA Chemicals Novapol® TF-Y534-IP Hexene LLDPE Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer	NOVA Chemicals
Trade Name	Novapol®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Novapol® TF-Y534-IP Hexene LLDPE Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Film Properties. Features: Excellent stiffness, excellent puncture, high strength and toughness.Applications: Industrial packaging, overwrap, narrow die gap extrusion.Data provided by the manufacturer.

Physical Properties	Metric	English	Comments
Density	0.934 g/cc	0.0337 lb/in³	ASTM D792
Thickness	25.4 microns	1.00 mil
Melt Flow	0.75 g/10 min @Load 2.16 kg, Temperature 190 °C	0.75 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	15.0 MPa	2180 psi	ASTM D882
Film Tensile Strength at Yield, TD	17.0 MPa	2470 psi	ASTM D882
Film Elongation at Break, MD	520 %	520 %	ASTM D882
Film Elongation at Break, TD	760 %	760 %	ASTM D882
Secant Modulus, MD	0.350 GPa	50.8 ksi	ASTM D882
Secant Modulus, TD	0.410 GPa	59.5 ksi	ASTM D882
Coefficient of Friction	0.38	0.38	ASTM D1894
Elmendorf Tear Strength, MD	2.00 g/micron	50.8 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	21.0 g/micron	533 g/mil	ASTM D1922
Dart Drop	2.80 g/micron	71.1 g/mil	F 50; ASTM D1709/A
Film Tensile Strength at Break, MD	44.0 MPa	6380 psi	ASTM D882
Film Tensile Strength at Break, TD	32.0 MPa	4640 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	9.0 % @Thickness 0.0250 mm	9.0 % @Thickness 0.000984 in	ASTM D1003
Gloss	63 %	63 %	45°; 1 mil; ASTM D1894