- ND Industries 567 Shaft & Bearing Retainer Retaining Compound
ND Industries 567 Shaft & Bearing Retainer Retaining Compound
| Category | Polymer , Adhesive , Thermoset |
| Manufacturer | ND Industries, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ND Industries 567 Shaft & Bearing Retainer Retaining Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High temperature retainer for engine cylinder liners and heat exchanger tubes
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 6300 - 7700 cP | 6300 - 7700 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Shear Strength | 13.8 - 20.7 MPa | 2000 - 3000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 10.0 min | 0.167 hour | With Primer (Fixture) |
| 30.0 min | 0.500 hour | On steel (Fixture) | |
| 1440 min | 24.0 hour | On Steel (Full) | |
| 1440 min | 24.0 hour | With Primer (Full) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Green | |
| Gap Fill, in. | 0.015 |
Users viewing this material also viewed the following:
- MV Labs PD780 [Pd(NH3)4](NO3)2 Tetraminepalladium(II) nitrate
- UBE J2522 Polyethylene
- A. Schulman SCHULAMID® 6 GF33 33% Glass Fiber Reinforced Nylon 6
- Chesterton MRS S2 Metal Rebuilding System
- ExxonMobil LLDPE LL 1001X26 Linear Low Density Polyethylene Resin
- Chosun Refractories SP-3000 High-Adhesion Mortar
- Aclo Accuguard Polycarbonate POL050G10HIV0L Glass Reinforced High Impact Flame Retardant
- Toyobo PELPRENE™ P40B Polyester TPE
- DuPont Fusabond® MB528D Linear Low Density Polyethylene (discontinued **)
- Americas Styrenics Styron® 612 Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved