Multibase Nylex™ 2185 NAT Polyamide + PP

Category Polymer , Thermoplastic , Nylon , Polypropylene (PP)
Manufacturer Multibase
Trade Name Nylex™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Nylex™ 2185 NAT Polyamide + PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Crack Resistance, GoodDimensional Stability, GoodImpact Resistance, GoodMoisture ResistantProcessability, GoodForms:PelletsProcessing Methods:Injection MoldingUses: Electrical PartsHousing, Electrical Safety EquipmentInformation provided by Multibase
Physical Properties Metric English Comments
Specific Gravity 0.970 g/cc
0.970 g/cc
ASTM 792
Water Absorption 0.65 %
0.65 %
ASTM D570
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM D955
Melt Flow 1.4 g/10 min
1.4 g/10 min
Cond. Q; ASTM D1238
4.7 g/10 min

@Load 2.16 kg,
Temperature 230 °C
4.7 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 40.1 MPa
5820 psi
ASTM D638
Elongation at Break 95 %
95 %
ASTM D638
Flexural Strength 47.5 MPa
6890 psi
ASTM D790
Flexural Modulus 1.43 GPa
207 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.908 J/cm
1.70 ft-lb/in
73°F; ASTM D256
Gardner Impact 11.298 J
8.3333 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 275 °C
527 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 205 °C
401 °F
Middle Barrel Temperature 208 °C
406 °F
Front Barrel Temperature 213 °C
415 °F
Nozzle Temperature 213 °C
415 °F
Mold Temperature 13.0 - 47.8 °C
55.4 - 118 °F
Injection Pressure 2.41 - 8.27 MPa
350 - 1200 psi
Back Pressure 0.345 - 1.03 MPa
50.0 - 150 psi
Descriptive Properties Value Comments
Injection Rate Moderate-Fast