Multibase Nylex™ 2185 HF Black Polyamide + PP
| Category | Polymer , Thermoplastic , Nylon , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Nylex™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Nylex™ 2185 HF Black Polyamide + PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms: PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | ASTM D955 |
| Melt Flow | 9.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 29.6 MPa | 4300 psi | ASTM D638 |
| Elongation at Break | 38 % | 38 % | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 1.45 GPa | 210 ksi | Method I (3 point load), Procedure B); ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 19.77 J | 14.58 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Polymer Industries Densetec HDPE Rod
- Shell Carilon® DB6F0A10 Polyketone, Flame-Retarded (V-0) Injection Molding Grade (discontinued **)
- Parker Chomerics SOFT-SHIELD® 4006 Low Closure Force, Foam Core EMI Gasket
- Loxim 330 12HSL Nylon 6
- LATI Latilub 66-15T G/30 PA66, 30% Glass Fiber Reinforced, PTFE Filled
- LATI Latiohm 83-07 PD11 CNT PA12, Impact Modified
- Taiwan PU Corporation TPUF Thermoplastic Polyurethane (TPU), 20% Glass Fiber Reinforced
- Epoxyset Epoxibond EB-309 Low Expansion Epoxy Adhesive
- 3M Scotch-Weld™ PR5 Plastic and Rubber Instant Adhesive
- NAPCO C90 Magnesite
Copyright © lookpolymers.com All Rights Reserved