Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 61
61
no post cure; ASTM D2240
74
74
post cured- 2 hours at 177°C; ASTM D2240
75
75
post cured- 4 hours at 177°C; ASTM D2240
77
77
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 7.012 MPa
1017 psi
post cured- 2 hours at 177°C; ASTM D412
7.274 MPa
1055 psi
post cured- 4 hours at 177°C; ASTM D412
7.329 MPa
1063 psi
post cured- 8 hours at 177°C; ASTM D412
8.053 MPa
1168 psi
no post cure; ASTM D412
Tensile Strength, Yield 2.45 MPa
355 psi
at 200%, no post cure; ASTM D412
3.36 MPa
487 psi
200%, post cured- 4 hours at 177°C; ASTM D412
3.36 MPa
487 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
3.77 MPa
547 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 583 %
583 %
post cured- 8 hours at 177°C; ASTM D412
672 %
672 %
post cured- 2 hours at 177°C; ASTM D412
691 %
691 %
post cured- 4 hours at 177°C; ASTM D412
939 %
939 %
no post cure; ASTM D412
Tear Strength 40.3 kN/m
230 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
41.0 kN/m
234 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
42.2 kN/m
241 pli
Die B, no post cure; ASTM D624
44.5 kN/m
254 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
Thermal Properties Metric English Comments
Shrinkage 2.0 %
2.0 %
no post cure
2.60 %

@Temperature 177 °C,
Time 7200 sec
 2.60 %

@Temperature 351 °F,
Time 2.00 hour
 post cured
2.60 %

@Temperature 177 °C,
Time 28800 sec
 2.60 %

@Temperature 351 °F,
Time 8.00 hour
 post cured
2.70 %

@Temperature 177 °C,
Time 14400 sec
 2.70 %

@Temperature 351 °F,
Time 4.00 hour
 post cured