Mitsubishi HostaphanÂ® RN, 15 micron Nominal Thickness Universal Polyethylene Terephthalate Film

Category	Polymer , Film , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer	Mitsubishi
Trade Name	Hostaphan®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Mitsubishi HostaphanÂ® RN, 15 micron Nominal Thickness Universal Polyethylene Terephthalate Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HostaphanÂ® RN is a transparent, biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties. HostaphanÂ® RN is the standard product for the following applications:Films for packagingCoatingLaminatingMetallizingPrintingDecorative filmsGloss laminationsAdhesive tapesInsulation tapesReleaseTransfer filmRelease film for thermosetting resingsHot stamping/Roll leafInformation provided by Mitsubishi Polyester Film

Physical Properties	Metric	English	Comments
Density	1.40 g/cc @Temperature 23.0 Â°C	0.0506 lb/inÂ³ @Temperature 73.4 Â°F	ASTM D1505-68, method C
Linear Mold Shrinkage	0.013 cm/cm @Temperature 150 Â°C, Time 900 sec	0.013 in/in @Temperature 302 Â°F, Time 0.250 hour	DIN 40634
Linear Mold Shrinkage, Transverse	0.0010 cm/cm @Temperature 150 Â°C, Time 900 sec	0.0010 in/in @Temperature 302 Â°F, Time 0.250 hour	DIN 40634

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	230 MPa	33400 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, MD	>= 110 %	>= 110 %	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, TD	100 %	100 %	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Modulus of Elasticity	4.40 GPa @Temperature 23.0 Â°C	638 ksi @Temperature 73.4 Â°F	MD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
	5.00 GPa @Temperature 23.0 Â°C	725 ksi @Temperature 73.4 Â°F	TD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Coefficient of Friction, Static	0.40	0.40	DIN 53375 or ASTM D1894

Optical Properties	Metric	English	Comments
Haze	4.0 %	4.0 %	Enlarged measurement angle; ASTM D1003-61, method A
Transmission, Visible	90 %	90 %	transparent; thickness not quantified

Descriptive Properties	Value	Comments
F5-value (MPa)	105	ISO 527-1, ISO 527-3; Sample type 2; TD; Test speed 100%/min.; 23ÂºC, 50% r.h.
	110	ISO 527-1, ISO 527-3; Sample type 2; MD; Test speed 100%/min.; 23ÂºC, 50% r.h.