Materion Brushform® 290 Beryllium Copper Alloy Strip; TM00 Temper (UNS C17200)
| Category | Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | Brushform® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion Brushform® 290 Beryllium Copper Alloy Strip; TM00 Temper (UNS C17200).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 97%Stress Relaxation after 1000 hrs @ 200°C: 76%Formability Ratio, 90° Bend, Radius/Thickness (Good Way): 0Formability Ratio (bad Way): 0Superficial Hardness: 30T 81-30N52Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.36 g/cc | 0.302 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | >= 98 | >= 98 | |
| Hardness, Rockwell C | <= 31 | <= 31 | |
| Hardness, Vickers | 225 - 309 | 225 - 309 | |
| Tensile Strength, Ultimate | >= 680 MPa | >= 98600 psi | |
| Tensile Strength, Yield | 510 - 670 MPa | 74000 - 97200 psi | |
| Elongation at Break | 19 - 35 % | 19 - 35 % | |
| Modulus of Elasticity | 131 GPa | 19000 ksi | |
| Fatigue Strength | 280 - 310 MPa @# of Cycles 1.00e+8 |
40600 - 45000 psi @# of Cycles 1.00e+8 |
Reverse Bending (R=1) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.0 µm/m-°C @Temperature 20.0 - 200 °C |
9.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 105 W/m-K | 729 BTU-in/hr-ft²-°F | |
| Melting Point | 870 - 980 °C | 1600 - 1800 °F | |
| Solidus | 870 °C | 1600 °F | |
| Liquidus | 980 °C | 1800 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Beryllium, Be | 1.8 - 2.0 % | 1.8 - 2.0 % | |
| Co + Ni | >= 0.20 % | >= 0.20 % | |
| Co + Ni + Fe | <= 0.60 % | <= 0.60 % | |
| Copper, Cu | 98 % | 98 % | as balance |
| Lead, Pb | <= 0.020 % | <= 0.020 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000660 - 0.0000101 ohm-cm | 0.00000660 - 0.0000101 ohm-cm | 17-26% IACS Conductivity |
Users viewing this material also viewed the following:
- RheTech Products T40P100-04 40% Talc Reinforced Polypropylene, White
- Indium Corp. #2212-35 Wave Solder Flux
- MetalTek MTEK 102-N Cast UNS C92900 Gear Bronze
- SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer
- Taiwan Sheen Soon Sheenthane® A9720 Thermoplastic Polyurethane Elastomer
- Williams Advanced Alloys WS314 Solder
- Loctite® 5083 Silicone Light Cure Adhesive
Copyright © lookpolymers.com All Rights Reserved