Materion Beryllium Copper Alloy 3 Wire; HT (TH04) Temper; 1.3-12.7 mm Diameter (UNS C17510)

Category	Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy
Manufacturer	Materion Corporation (former Brush Wellman)
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Materion Beryllium Copper Alloy 3 Wire; HT (TH04) Temper; 1.3-12.7 mm Diameter (UNS C17510).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Treatment required for max strength: 2 hrs @ 480-495°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.

Physical Properties	Metric	English	Comments
Density	8.83 g/cc	0.319 lb/in³

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	750 - 970 MPa	109000 - 141000 psi
Tensile Strength, Yield	650 - 870 MPa	94300 - 126000 psi
Elongation at Break	>= 10 %	>= 10 %
Modulus of Elasticity	138 GPa	20000 ksi

Thermal Properties	Metric	English
CTE, linear	18.0 µm/m-°C @Temperature 20.0 - 200 °C	10.0 µin/in-°F @Temperature 68.0 - 392 °F
Thermal Conductivity	240 W/m-K	1670 BTU-in/hr-ft²-°F
Melting Point	1040 - 1080 °C	1900 - 1980 °F
Solidus	1040 °C	1900 °F
Liquidus	1080 °C	1980 °F

Component Elements Properties	Metric	English	Comments
Beryllium, Be	0.20 - 0.60 %	0.20 - 0.60 %
Copper, Cu	98 %	98 %	as balance
Nickel, Ni	1.4 - 2.2 %	1.4 - 2.2 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.00000290 - 0.00000360 ohm-cm	0.00000290 - 0.00000360 ohm-cm	48-60% IACS Conductivity