Aclo Accutech Polypropylene Homopolymer HP0339G40CL Glass Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339G40CL Glass Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 89.98 MPa | 13050 psi | ASTM D638 |
| Tensile Strength, Yield | 87.01 MPa | 12620 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 4.599 GPa | 667.1 ksi | ASTM D638 |
| Flexural Strength | 118.0 MPa | 17110 psi | ASTM D790 |
| Flexural Modulus | 7.4987 GPa | 1087.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F |
Users viewing this material also viewed the following:
- LG Chemical LUMID HI5001AS PA6/PO, High Barrier Property, CaCl2 Resistance, High Impact
- LG Chemical LUPOL HF5254A PP+MF20%
- Lucas-Milhaupt SIL-FOS 18 Silver/ Copper/ Phosphorus Alloy
- Kuraray HYBRAR® SC1
- Star Plastics PC1510R Molding Grade PC with Release
- SABIC Innovative Plastics NORYL NC212 PPE+HIPS (Asia Pacific)
- Arlon 51601W015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Eastman E6838-975F Polyethylene (discontinued **)
- Polimeri Europa KOBLEND PCA 447F PC+ABS (discontinued **)
Copyright © lookpolymers.com All Rights Reserved