- Materion Beryllium Copper Alloy 25 Strip; H (TD04) Temper (UNS C17200)
Materion Beryllium Copper Alloy 25 Strip; H (TD04) Temper (UNS C17200)
| Category | Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion Beryllium Copper Alloy 25 Strip; H (TD04) Temper (UNS C17200).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Treatment required for max strength: as suppliedFormability Ratio, 90° Bend, Radius/Thickness (Good Way): 1Formability Ratio (bad Way): 2.9Superficial Hardness: 30T 79-83Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.36 g/cc | 0.302 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 96 - 102 | 96 - 102 | |
| Hardness, Vickers | 216 - 287 | 216 - 287 | |
| Tensile Strength, Ultimate | 680 - 830 MPa | 98600 - 120000 psi | |
| Tensile Strength, Yield | 620 - 800 MPa | 89900 - 116000 psi | |
| Elongation at Break | 2.0 - 18 % | 2.0 - 18 % | |
| Modulus of Elasticity | 131 GPa | 19000 ksi | |
| Fatigue Strength | 240 - 270 MPa @# of Cycles 1.00e+8 |
34800 - 39200 psi @# of Cycles 1.00e+8 |
Reverse Bending (R=1) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.0 µm/m-°C @Temperature 20.0 - 200 °C |
9.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 105 W/m-K | 729 BTU-in/hr-ft²-°F | |
| Melting Point | 870 - 980 °C | 1600 - 1800 °F | |
| Solidus | 870 °C | 1600 °F | |
| Liquidus | 980 °C | 1800 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Beryllium, Be | 1.8 - 2.0 % | 1.8 - 2.0 % | |
| Co + Ni | >= 0.20 % | >= 0.20 % | |
| Co + Ni + Fe | <= 0.60 % | <= 0.60 % | |
| Copper, Cu | 98 % | 98 % | as balance |
| Lead, Pb | <= 0.020 % | <= 0.020 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000910 - 0.0000115 ohm-cm | 0.00000910 - 0.0000115 ohm-cm | 15-19% IACS Conductivity |
Users viewing this material also viewed the following:
- Iran Petrochemical (PCC) T 30 S Polypropylene
- Kaiser 7068 T6, T6511 Rod & Bar
- Lucite International Colacryl ® DP300 Specialty Acrylic Resin
- Borealis Borstar® BB2581 HDPE for Blow Molding
- Zoltek Panex 35® Uni-Directional Carbon Fiber Prepreg
- ExxonMobil Exceed™ 1018KB Metallocene Polyethylene Resin (European Grade)
- DuPont™ Kapton® 300HN Polyimide Film, 75 Micron Thickness
- 3M Scotch® 898 Filament Tape
- LATI LARPEEK 50 G/50 50% Glass Reinforced Polyetheretherketone (PEEK) (discontinued **)
- Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate
Copyright © lookpolymers.com All Rights Reserved