Master Bond EP51FL-1 Rapid Curing Cryogenic Two Component Epoxy

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Master Bond Inc.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Master Bond EP51FL-1 Rapid Curing Cryogenic Two Component Epoxy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Master Bond Polymer System EP51FL-1 is a two component highly flexible epoxy resin system for high performance bonding sealing and coating. Although most flexiblilized epoxy formulations are very slow curing, EP51FL-1 offers a relatively rapid cure, with a setup time in most cases of about 30-40 minutes and full cure within 24 hours at room temperature. EP51FL-1 has been used in cryogenic applications as both an adhesive and sealant. Its service temperature range is 4K to 250°F.

Physical Properties	Metric	English	Comments
Viscosity	70000 - 80000 cP	70000 - 80000 cP

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	55 - 60	55 - 60
Hardness, Shore D	12 - 15	12 - 15
Tensile Strength	7.93 MPa	1150 psi
Elongation at Break	>= 125 %	>= 125 %
Shear Strength	>= 6.89 MPa	>= 1000 psi	Tensile, Al/Al
Peel Strength	>= 6.14 kN/m	>= 35.0 pli

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	48.9 °C	120 °F
Minimum Service Temperature, Air	-269 °C	-452 °F

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm

Processing Properties	Metric	English	Comments
Cure Time	60.0 - 120 min @Temperature 93.3 °C	1.00 - 2.00 hour @Temperature 200 °F
	1440 min @Temperature 23.9 °C	24.0 hour @Temperature 75.0 °F
Pot Life	15 - 20 min	15 - 20 min	100 gm mass
Shelf Life	12.0 Month	12.0 Month	in unopened containers

Descriptive Properties	Value	Comments
Mixing Ratio (A to B)	1:3