Malvern Minerals Sliastic 740 with 33% Novacite® L-207A Quartz Filler

Category Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber
Manufacturer Malvern Minerals Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Malvern Minerals Sliastic 740 with 33% Novacite® L-207A Quartz Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Press Vulcanized 5 minutes at 260° F. Product data demonstrates the effect of the Novacite® filler.Information provided by Malvern Minerals Company.
Mechanical Properties Metric English Comments
Hardness, Shore A 50
50
Post oven cured 24 hours at 480°F
52
52
Oven cured 4 hours at 480°F
Tensile Strength at Break 4.14 MPa
600 psi
Oven cured 4 hours at 480°F
5.65 MPa
820 psi
Post oven cured 24 hours at 480°F
Elongation at Break 260 %
260 %
Oven cured 4 hours at 480°F
270 %
270 %
Post oven cured 24 hours at 480°F
Tear Strength 8.41 kN/m
48.0 pli
Die B
8.77 kN/m
50.0 pli
Die B
Compression Set 5.9 %

@Temperature 177 °C,
Time 79200 sec
 5.9 %

@Temperature 350 °F,
Time 22.0 hour
 Post oven cured 24 hours at 480°F
16 %

@Temperature 177 °C,
Time 79200 sec
 16 %

@Temperature 350 °F,
Time 22.0 hour
 Oven cured 4 hours at 480°F