M. Holland Company MAGMA® LM311-D LLDPE (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | M. Holland Company MAGMA® LM311-D LLDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good Processability, Good Puncture Resistance, Good Tear Strength, Good ToughnessProcessing Method: ExtrusionInformation provided by M. Holland.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.885 g/cc | 0.0320 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 950 % | 950 % | ASTM D882 |
| Film Elongation at Break, TD | 1100 % | 1100 % | ASTM D882 |
| Elmendorf Tear Strength MD | 580 g | 580 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 820 g | 820 g | ASTM D1922 |
| Dart Drop Test | >= 1000 g | >= 2.20 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 52.4 MPa | 7600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 44.3 MPa | 6420 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 80.0 °C | 176 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | <= 154 °C | <= 310 °F | |
| Zone 1 | 154 °C | 310 °F | |
| Melt Temperature | 166 - 204 °C | 330 - 400 °F | |
| Die Opening | 0.0810 - 0.254 cm | 0.0319 - 0.100 in | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets |
Users viewing this material also viewed the following:
- Techmer ES Electrablend® ABS 04001 BK 10% Stainless Steel Filled
- A. Schulman POLYBATCH™ White LL8350 AP Concentrate Based In LLDPE
- A. Schulman POLYBATCH™ Brown 10305U Concentrate Based In LLDPE
- UBE UBESTA® 3030U Nylon 12 (After Fuel C/E10 for 1000 hours)
- Loctite® Output™ 5404 Heat Cure Silicone
- Dow Corning SE 1815 CV KIT
- Covestro Makrolon® 2467 Polycarbonate
- CLAL-MSX SICLANIC S® TH4 Quenched Copper Alloy, 4/4 Hard, precipitation treated
- 3M Scotch® 214 High-Temperature Masking Tape
Copyright © lookpolymers.com All Rights Reserved