M. Holland Company MAGMA® LM203-C LLDPE (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | M. Holland Company MAGMA® LM203-C LLDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good Heat Seal, Good Tear Strength, Good ToughnessUses: BlendingProcessing Method: ExtrusionInformation provided by M. Holland.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | 810 % | 810 % | ASTM D882 |
| Elmendorf Tear Strength MD | 600 g | 600 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 700 g | 700 g | ASTM D1922 |
| Dart Drop Test | >= 850 g | >= 1.87 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 44.8 MPa | 6500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 93.3 °C | 200 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | <= 149 °C | <= 300 °F | |
| Zone 1 | 149 °C | 300 °F | |
| Melt Temperature | 182 - 232 °C | 360 - 450 °F | |
| Die Opening | 0.0810 - 0.254 cm | 0.0319 - 0.100 in | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets |
Users viewing this material also viewed the following:
- LG Chemical SHP-IPA ISOPROPYL ALCOHOL
- Sharadaa Ceramics HF 60 AL Insulation Brick
- Styron Magnumâ„¢ 2610 ABS, High Gloss
- CeramTec Ceramtape A Alumina for Constrained Sintering
- BASF Ultradur® B 4406 G3 Uncolored Q717 PBT
- Arlon 51986R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Alliance S-32 Samarium Cobalt Magnetic Material
- 3M Scotch-Weld™ LSB60NS Toughened Epoxy Adhesives
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Non-Black, Oyster Shell Calcium Carbonate
Copyright © lookpolymers.com All Rights Reserved