BASF Polystyrol® 2712 Impact Grade Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 2712 Impact Grade Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flowing special grade, particularly resistant to stress cracking.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | |
| Elongation at Break | 40 % | 40 % | |
| Elongation at Yield | 1.4 % | 1.4 % | |
| Tensile Modulus | 1.40 GPa | 203 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 12.0 J/cm² @Temperature -30.0 °C |
57.1 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Vicat Softening Point | 83.0 °C | 181 °F | |
| Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.00010 @Frequency 1e+6 Hz |
0.00010 @Frequency 1e+6 Hz |
|
| Comparative Tracking Index | 500 V | 500 V |
Users viewing this material also viewed the following:
- Garlock MULTI-SWELLâ„¢ 3760 Compressed Aramid Fiber Gasketing
- Techmer ES Electrablend® PA6/6 GF13 SS10 BK 13/10% Glass/Stainless Steel Filled
- Techmer ES Electrafil® J-4/25/CF/15 NAT PA6/12
- Techmer ES HiFill® PA6/6 GF55 L BK 55% Glass Filled
- TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 1.75 - 2.50 in Rod or Thickness; Per ASTM F136)
- A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT
- Teknor Apex TEKRON® 4000-60 Thermoplastic Elastomer
- Arlon 51570R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- DSM Akulon® K223-P2 Impact Modified Nylon 6 (European Grade) (Cond)
- Total Finathene® WR 201 B HDPE blow molding (discontinued **)
Copyright © lookpolymers.com All Rights Reserved