LyondellBasell Hostacom™ PF062-3 Polypropylene Homopolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer	LyondellBasell
Trade Name	Hostacom™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Hostacom™ PF062-3 Polypropylene Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Hostacom™ PF062-3 high melt flow, 5,200 MPa flexural modulus, chemically coupled, 30% glass fiber-reinforced polypropylene homopolymer has good impact strength, high stiffness and very good mold filling capability. Uses: Appliances, automotive applications, electrical partsInformation provided by Basell.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³	ASTM D792
Melt Flow	20 g/10 min @Load 2.16 kg, Temperature 230 °C	20 g/10 min @Load 4.76 lb, Temperature 446 °F	Condition L; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	90.3 MPa	13100 psi	ASTM D 638
Elongation at Yield	2.2 %	2.2 %	ASTM D 638
Flexural Yield Strength	143 MPa	20800 psi	ASTM D790
Flexural Modulus	5.20 GPa	754 ksi	Tangent, 0.05 in/min; ASTM D790
Izod Impact, Notched	0.849 J/cm	1.59 ft-lb/in	73°F; ASTM D256
Izod Impact, Unnotched	5.93 J/cm	11.1 ft-lb/in	73°F; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	161 °C	322 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	151 °C	303 °F	Unannealed; ASTM D648
UL RTI, Electrical	230 °C	446 °F	0.0625 in; UL 746
UL RTI, Mechanical with Impact	230 °C	446 °F	0.0625 in; UL 746
UL RTI, Mechanical without Impact	230 °C	446 °F	0.0625 in; UL 746
Flammability, UL94	HB @Thickness 1.59 mm	HB @Thickness 0.0626 in