ExxonMobil HD 8660.29 Rotational Molding Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Rotational Molding Grade
Manufacturer	Exxon Chemical
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil HD 8660.29 Rotational Molding Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: HD 8660 series are high density hexane copolymers designed to offer superior toughness and stiffness. They are ideally suited for applications that require the optimum balance of low temperature toughness, creep resistance, stiffness, ESCR and tear properties.Availability: Latin America, North America and South America Additive: Long Term UV-15 Stabilizer: YesApplications: Industrial ProductsIntermediate Bulk ContainersLarge Agricultural TanksInformation provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.942 g/cc	0.0340 lb/in³	ASTM D4883
ESCR 100% Igepal®	550 hour	550 hour	ASTM D1693 Condition A
ESCR 10% Igepal®	50 hour	50 hour	ASTM D1693 Condition A
Melt Flow	2.00 g/10 min @Load 2.16 kg, Temperature 190 °C	2.00 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	20.0 MPa	2900 psi	2.0 in/min; ASTM D638
Elongation at Yield	20 %	20 %	2.0 in/min; ASTM D638
Flexural Modulus	0.896 GPa	130 ksi	1% Secant; ASTM D790
Impact Test	108 J @Thickness 3.17 mm, Temperature -40.0 °C	80.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM
	244 J @Thickness 6.35 mm, Temperature 25.0 °C	180 ft-lb @Thickness 0.250 in, Temperature 77.0 °F	ARM

Thermal Properties	Metric	English	Comments
Melting Point	129 °C	264 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	67.0 °C	153 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	41.0 °C	106 °F	ASTM D648

Descriptive Properties	Value	Comments
Features	Long Term UV 8 Stabilization
Form	Pellet