LyondellBasell Hostacomâ„¢ CB271FC Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hostacom™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hostacomâ„¢ CB271FC Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hostacomâ„¢ CB271FC high melt flow, 2,400 MPa flexural modulus, precolored, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of stiffness, impact resistance and processability. It was designed primarily for automotive interior applications that demand balanced performance characteristics, such as those that require compliance to FMVSS201 or FMVSS208. Uses: Automotive interior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 78 | 78 | ISO 2039-2 |
| Hardness, Shore D | 71 | 71 | ISO 868 |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO 527-1, -2 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527-1, -2 |
| Elongation at Break | 60 % | 60 % | ISO 527-1, -2 |
| Elongation at Yield | 11 % | 11 % | ISO 527-1, -2 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.30 kJ/m² @Temperature -30.0 °C |
1.57 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 24.0 kJ/m² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.2 °C | 171 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.60 % | 0.60 % | Tool, 100x150x3.2 mm; Basell Test Method |
Users viewing this material also viewed the following:
- RheTech Products FT4600-152 Thermoplastic Polyolefin, UV Stabilized, JA6A Black
- Performance Polymers IPS II PPL-C4250 PEKK (Polyetherketoneketone) Linear 30% Carbon Fiber Reinforced Molding Grade
- H.C. Starck Grade UF 15 Premix Silicon Carbide, SiC
- LyondellBasell Higlass BJ22GC Polypropylene Copolymer, 30% Glass Fiber
- UBE F222 Polyethylene
- Unifrax Fiberfrax® Duraboard® 500ES Ceramic Fiber Board
- TriStar FCJ Composite Bearing
- BASF Ultramid® SEGM35 H1 BK 6259 40% Glass/Mineral Filled PA6 (Dry)
- ATI Allvac® Nickelvac® 606 Nickel Superalloy
Copyright © lookpolymers.com All Rights Reserved