- LyondellBasell Hostacomâ„¢ CB189FC/1 Thermoplastic Polyolefin Elastomer
LyondellBasell Hostacomâ„¢ CB189FC/1 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hostacom™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hostacomâ„¢ CB189FC/1 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hostacomâ„¢ CB189FC/1 medium melt flow, 1,300 MPa flexural modulus, precolored, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of impact, stiffness, dimensional stability and processability. It was designed specifically for use in various automotive interior trim components. Uses: Automotive interior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 1183 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527-1, -2 |
| Elongation at Yield | 10 % | 10 % | ISO 527-1, -2 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.80 kJ/m² @Temperature -40.0 °C |
1.33 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 5.80 kJ/m² @Temperature 10.0 °C |
2.76 ft-lb/in² @Temperature 50.0 °F |
ISO 180 | |
| 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Gardner Impact | 16.0 J @Temperature -30.0 °C |
11.8 ft-lb @Temperature -22.0 °F |
ASTM D3029 |
| 25.0 J @Temperature 23.0 °C |
18.4 ft-lb @Temperature 73.4 °F |
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.2 °C | 189 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 °C | 127 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 1.0 % | 1.0 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.40 % @Temperature 121 °C, Time 3600 sec |
1.40 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- MV Labs CD1000 CdSO4·xH2O Cadmium sulfate hydrate
- LyondellBasell Petrothene® GA502024 Linear Low Density Polyethylene
- Ineos J60-800-178 HDPE
- Solvay Specialty Polymers Cogegum® GFR/350 Polyolefin
- Samsung Cheil Industries Starex® MG-0330 ABS, Unreinforced Heat Resistant
- Chase Plastics CP Pryme® AH120 Acetal Copolymer, 20% Glass Fiber Reinforced
- Braskem F020HC High Crystallinity Polypropylene Homopolymer
- Arlon Thermabond®-II 99760N015 0.015" (0.381 mm) Unsupported/Uncured Silicone Rubber with Fiberglass Substrate
- Amity Thermosets ATM 122 Phenolic Molding Organic Filler, Compression Molded
Copyright © lookpolymers.com All Rights Reserved