LyondellBasell Higlass PF072-3 Polypropylene Homopolymer, 30% Glass Fiber

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	LyondellBasell
Trade Name	Higlass
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Higlass PF072-3 Polypropylene Homopolymer, 30% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features: conventional melt flow, high modulus, chemically coupled, glass fiber-reinforced polypropylene homopolymer, high rigidity, high strength, good impact resistanceApplications: appliance parts, automotive components, pump housings, athletic equipmentDescription: Higlass PF072-3 high melt flow, chemically coupled, 30% glass fiber-reinforced polypropylene homopolymer has a very good balance of strength, stiffness and impact resistance.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/inÂ³	ASTM D792
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in	Tool, Montell
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 230 Â°C	2.0 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	97.0 MPa	14100 psi	ASTM D638
Elongation at Break	2.0 %	2.0 %	ASTM D638
Flexural Modulus	6.20 GPa	899 ksi	Tangent at 0.05 in/min; ASTM D790A
Izod Impact, Notched	1.10 J/cm	2.06 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	160 Â°C	320 Â°F	ASTM D648