LyondellBasell Hifaxâ„¢ CB229 Thermoplastic Olefin Resin
| Category | Polymer , Thermoplastic |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CB229 Thermoplastic Olefin Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: medium high melt flow, medium high modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, excellent processability, good paintabilityApplications: automotive claddings and rocker panels, end caps, appliquesDescription: Hifax CB229 medium melt flow, mineral-filled thermoplastic elastomeric olefin resin has an excelent combination of flow, stiffness, paintability and dynamic impact characteristics. It was designed primarily for automotive exterior ornamentation applications.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Tool, Montell |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ISO R527-1 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO R527-1 |
| Elongation at Break | >= 500 % | >= 500 % | ISO R527-1 |
| Elongation at Yield | 10 % | 10 % | ISO R527-1 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ISO 180 |
| Impact Test | 24.0 J @Temperature -30.0 °C |
17.7 ft-lb @Temperature -22.0 °F |
MAII, E at Max Load, Ductile; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 66.0 µm/m-°C @Temperature -30.0 - 100 °C |
36.7 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
Users viewing this material also viewed the following:
- Omni Plastics OmniLon™ 6 PA6 WF30 Mineral Filled Nylon
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 3.0 PHR Thanecure ZM
- LyondellBasell Alathon® H6017 High Density Polyethylene, Injection Molding Grade
- Fujipoly Industries Sarcon® NR-c Gap Filler Pad Non-Silicone
- Multibase 7-9600 Dow-Corning Soft Filling Elastomer Parts A and B
- A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass)
- Westlake EM800AA Low Density Polyethylene
- Trelleborg S761 Silicone Rubber
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7330-1000 TPE
Copyright © lookpolymers.com All Rights Reserved