- Lucent Polymers TPP-340 Polypropylene, 40% Talc Filled, Impact Modified
Lucent Polymers TPP-340 Polypropylene, 40% Talc Filled, Impact Modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers TPP-340 Polypropylene, 40% Talc Filled, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.01 cm/cm @Thickness 3.17 mm |
0.01 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.14 MPa | 3501 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 46.9 MPa | 6800 psi | ASTM D790 |
| Flexural Modulus | 2.897 GPa | 420.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.335 J/cm @Thickness 3.17 mm |
2.501 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.67 °C | 170.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs CO200 CoBr2 Cobalt(II) bromide
- NOVA Chemicals Sclair® 8405 UV8D, 8405G UV8D MDPE Rotational Molding Resin (discontinued **)
- Huntsman IROGRAN® A 70 E 4675 Polyester-Based TPU-High Performance Grade
- Lord Adhesives 5181 High Viscosity, Black, General Purpose Ethyl Cyanoacrylate Adhesive
- Mitsui APELâ„¢ APL8008T Cyclo Olefin Copolymer (COC)
- Master Bond UV10FL-1 Flexibilized One Component UV Curable Adhesive
- A. Schulman POLYTROPE™ TPP 530 Injection Molding Grade Olefinic Thermoplastic Elastomer
- A. Schulman POLYPUR™ FPU 1103F Thermoplastic Polyurethane Compound
- Domo 2600M Polypropylene Copolymer
- Bapolene® 1057EC Low Density Polyethylene Extrusion Coating
Copyright © lookpolymers.com All Rights Reserved