Lucent Polymers TPP-240 Polypropylene, 40% Talc Filled, Impact Modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers TPP-240 Polypropylene, 40% Talc Filled, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.17 mm |
0.010 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.59 MPa | 4002 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 50.37 MPa | 7306 psi | ASTM D790 |
| Flexural Modulus | 3.241 GPa | 470.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.44 °C | 175.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GMF 604 40 UV Black 115 1 X 1 Polyamide 6 (Nylon 6)
- Poco Graphite TRA Semiconductor Grade Graphite
- Silberline Silvet® 320-20-J
- Covestro Bayflex® 180 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- Aleris Hokotol Aluminum Alloy, 200 mm Thickness
- 3M FP012602 White Polyester Label Products
- BASF Procom® C40H 458 Polypropylene
- Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction
- Saint-Gobain Korel® K60 Firm Micro-cellular Polyurethane Foam
Copyright © lookpolymers.com All Rights Reserved