- Lucent Polymers TPP-120 Polypropylene, Homopolymer, 20% Talc Filled
Lucent Polymers TPP-120 Polypropylene, Homopolymer, 20% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers TPP-120 Polypropylene, Homopolymer, 20% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 3.17 mm |
0.012 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 51.03 MPa | 7401 psi | ASTM D790 |
| Flexural Modulus | 2.2069 GPa | 320.08 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.67 °C | 170.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- DuPont Bynel® 4003 Anhydride-Modified HDPE Adhesive Resin (discontinued **)
- Ineos ABS Centrex® 813 ASA+AES Blend (discontinued **)
- LATI Latigloss 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized
- Saint-Gobain CHR® SG05-03(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Techmer ES Plaslube® J-50/20/TF/10 Polycarbonate, 20% GFR, 10% PTFE
- Borealis Nepol™ GB303HP 30% Long Glass Fiber Reinforced Polypropylene
- Trelleborg AEM Eccospheres® SI-130 Sodium Borosilicate Glass Microspheres
- Dow C700-35N Polypropylene Impact Copolymer Resin
- Asahi Kasei Tenac®-C 8520 Copolymer Acetal Resin
- Asahi Glass Fluon® RB1020S 20% Glass Fiber, PTFE Filled Compound
Copyright © lookpolymers.com All Rights Reserved