- Polypropylene, Impact Modified; Molded/Extruded
- Lucent Polymers PPC-220 Polypropylene, Impact Modified
Lucent Polymers PPC-220 Polypropylene, Impact Modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers PPC-220 Polypropylene, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.17 MPa | 4811 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 37.93 MPa | 5501 psi | ASTM D790 |
| Flexural Modulus | 1.034 GPa | 150.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 51.67 °C | 125.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-MASK II HT Conductive Foil Tape
- Polymer Resources PC/ABS-FR1-[color]-3 PC Blend, Flame Retardant, Standard Flow, UV Stabilized
- Polymax® Maxelast® C4990 TPE, Transparent
- Huntsman KRYSTALFLEX® PE 429 Polyurethane Optical Aliphatic Film
- Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F)
- Ineos L80Z-00 Impact Copolymer Polypropylene
- A. Schulman CP80-01 Linear Low-Density Polyethylene
- 3M 7901 Screen Printable Sheet Vinyl Label Material
- Tipco Tipcolene® HR 7222 - 25% Talc/Mineral Reinforced, Impact Modified Polypropylene Copolymer Compound
Copyright © lookpolymers.com All Rights Reserved