Lucent Polymers PC/PBT-1550 Polycarbonate+PBT, Improved Impact Resistance, Injection Grade

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Lucent Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lucent Polymers PC/PBT-1550 Polycarbonate+PBT, Improved Impact Resistance, Injection Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.014 cm/cm

@Thickness 3.17 mm
 0.014 in/in

@Thickness 0.125 in
 1/8" Section
Melt Flow 50 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 50 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 46.9 MPa
6800 psi
ASTM D638
Elongation at Break >= 128 %
>= 128 %
ASTM D638
Flexural Strength 75.86 MPa
11000 psi
ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
ASTM D790
Izod Impact, Notched 4.27 J/cm

@Thickness 3.17 mm,
Temperature -30.0 °C
 8.00 ft-lb/in

@Thickness 0.125 in,
Temperature -22.0 °F
 ASTM D256
8.01 J/cm

@Thickness 3.17 mm,
Temperature 22.8 °C
 15.0 ft-lb/in

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 86.67 °C
188.0 °F
ASTM D648