Lucent Polymers PC/ABS-1003 Polycarbonate+ABS, Extrusion / General Purpose, Injection Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers PC/ABS-1003 Polycarbonate+ABS, Extrusion / General Purpose, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.17 mm |
0.0070 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.79 MPa | 7802 psi | ASTM D638 |
| Elongation at Break | >= 120 % | >= 120 % | ASTM D638 |
| Flexural Strength | 82.76 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.276 GPa | 330.1 ksi | ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
6.00 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 |
| 5.34 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
10.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 115.56 °C | 240.01 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Plaskolite Optix® CP - 1000 I High Impact Grade Acrylic Resin
- Kolon ELLAS K-260D Thermoplastic Polyurethane
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours
- Styron CALIBREâ„¢ 300EP 22 Polycarbonate, General Purpose
- Cytec Thornel® Graphite Cloth Laminate with Mil R-9299 Resin
- Chosun Refractories SAL90N Special High Alumina brick
- Arlon 930-125Rxx-P0 0.030" (0.762 mm) Self-Fusing Silicone Tape
- Bhansali Engineering Abstron HI40H ABS Injection Molding Grade
- Total LDPE 1022 FN 24 Low Density Polyethylene - Blown Film
Copyright © lookpolymers.com All Rights Reserved