Lucent Polymers GPCB-120 Polycarbonate+PBT, 20% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers GPCB-120 Polycarbonate+PBT, 20% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 260 °C |
15 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 93.79 MPa | 13600 psi | ASTM D638 |
| Elongation at Break | >= 4.0 % | >= 4.0 % | ASTM D638 |
| Flexural Strength | 151.72 MPa | 22005 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
0.800 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ DP-9156-5-8000 Polypropylene Copolymer (PP Copolymer)
- Garlock 3205 Neoprene/Polyester Fabric
- Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet
- Haynes 282® Nickel Alloy Sheet, Solution Annealed and Cold Worked
- Silberline A-6209
- Plenco 7200 Phenolic, Granular, Injection Molded
- Zeon Chemicals Nipol® 35-8 Nitrile Elastomer
- A. Schulman POLYBATCH™ Blue LL40434 Concentrate Based In LLDPE
- Fainplast Compounds PG 56/B Flexible PVC, Extrusion Modified with Rubber
Copyright © lookpolymers.com All Rights Reserved