- Lubrizol Pellethane® 2363-55D Thermoplastic Polyurethane Elastomer
Lubrizol Pellethane® 2363-55D Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Pellethane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Pellethane® 2363-55D Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 1.60 mm |
0.0040 - 0.0080 in/in @Thickness 0.0630 in |
|
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm @Thickness 1.60 mm |
0.0050 - 0.0060 in/in @Thickness 0.0630 in |
|
| Melt Flow | 8.0 - 18 g/10 min @Load 2.16 kg, Temperature 224 °C |
8.0 - 18 g/10 min @Load 4.76 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 51 - 59 | 51 - 59 | ASTM D2240 |
| Tensile Strength, Ultimate | 47.5 MPa | 6890 psi | ASTM D412 |
| Elongation at Break | 30 % | 30 % | ASTM D412 |
| 390 % | 390 % | ASTM D412 | |
| 50% Modulus | 0.0131 GPa | 1.90 ksi | ASTM D412 |
| 100% Modulus | 0.0172 GPa | 2.49 ksi | ASTM D412 |
| 300% Modulus | 0.0295 GPa | 4.28 ksi | ASTM D412 |
| Flexural Modulus | 0.172 GPa | 24.9 ksi | ASTM D790 |
| Tear Strength | 114 kN/m | 650 pli | Die "C"; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 80 | 80 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 25 % @Temperature 25.0 °C, Time 79200 sec |
25 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395 Method B |
| 30 % @Temperature 70.0 °C, Time 79200 sec |
30 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 143 µm/m-°C @Temperature 20.0 °C |
79.4 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Vicat Softening Point | 109 °C | 228 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 225 °C | 410 - 437 °F | Molding |
| Mold Temperature | 15.0 - 60.0 °C | 59.0 - 140 °F | |
| Drying Temperature | 90.0 - 105 °C | 194 - 221 °F |
Users viewing this material also viewed the following:
- Polimeri Europa Eraclene® FC 82 High Density Polyethylene - Blown Film Extrusion
- Chevron Phillips KN 230 LDPE Injection Molding Resin (discontinued **)
- Lord Adhesives 5181 High Viscosity, Black, General Purpose Ethyl Cyanoacrylate Adhesive
- Greene Tweed CHEMRAZ® 584 Perfluoroelastomer
- Solvay Specialty Polymers Polymist® XPP 546 Polytetrafluoroethylene (PTFE)
- Dow DOWLEX™ 2045.11G Linear Low Density Polyethylene
- DuPont Performance Polymers Zytel® RS 30G30HSL BK038A Nylon 610
- 3M 7847 Laser Markable Label Material
- Asahi Kasei Thermofil P-20TC-5103 20% Talc Reinforced, Lubricated, Heat Stabilized
- Dielectric Polymers TRANS-SIL® NT-1005 Silicone Transfer Adhesive (discontinued **)
Copyright © lookpolymers.com All Rights Reserved