- Hexcel® HexPly® 954-6 Curing Cyanate Resin, K13C-2U Fiber
Hexcel® HexPly® 954-6 Curing Cyanate Resin, K13C-2U Fiber
| Category | Polymer , Thermoset , Epoxy |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® 954-6 Curing Cyanate Resin, K13C-2U Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 19.0 MPa @Temperature 23.0 °C |
2760 psi @Temperature 73.4 °F |
90° |
| 1799 MPa @Temperature 23.0 °C |
260900 psi @Temperature 73.4 °F |
0° | |
| Tensile Modulus | 4.80 GPa @Temperature 23.0 °C |
696 ksi @Temperature 73.4 °F |
90° |
| 556 GPa @Temperature 23.0 °C |
80600 ksi @Temperature 73.4 °F |
0° | |
| Compressive Yield Strength | 365 MPa @Temperature 23.0 °C |
52900 psi @Temperature 73.4 °F |
|
| Compressive Modulus | 558 GPa @Temperature 23.0 °C |
80900 ksi @Temperature 73.4 °F |
|
| Shear Strength | 44.0 MPa @Temperature 22.0 °C |
6380 psi @Temperature 71.6 °F |
0°, IL |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPH-20C UV Natural Polypropylene Homopolymer (PP Homopolymer)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Monoplex DOS Plasticizer
- 3M Dyneon™ TF 4105 PTFE 25% Glass Fiber Filled (discontinued **)
- Hybrid Plastics Nanoreinforced® POSS® Polyimide
- H.C. Starck Amperit® 583.054 Chromium Carbide-Nickel 83-17 (Cr3C2-Ni)
- Tisan TISETILEN® Flame Retardant (V0) Polyethylene
- Chevron Phillips Marlex® K605 HDPE Blow Molding Resin
- CP-Polymer-Technik Wellamid® 6000 GV 15 HWCP 15% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- EMS-Grivory Grivory® TRV-4X9 PAMACM12-GF40
Copyright © lookpolymers.com All Rights Reserved