Lubrizol Estane® 2355-95AE Thermoplastic Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® 2355-95AE Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formerly PellethaneFeature: Fuel resistant, extrusion laminate coatingAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by Dow Chemical.Lubrizol acquired the Pellethane product line from Dow in 2009.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0090 cm/cm
0.0050 - 0.0090 in/in
ASTM D955
Melt Flow 13 g/10 min

@Load 8.70 kg,
Temperature 190 °C
13 g/10 min

@Load 19.2 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 94
94
ASTM D2240
Tensile Strength, Ultimate 38.9 MPa
5640 psi
ASTM D412
Elongation at Break 450 %
450 %
ASTM D412
50% Modulus 0.00827 GPa
1.20 ksi
ASTM D412
100% Modulus 0.00965 GPa
1.40 ksi
ASTM D412
300% Modulus 0.0214 GPa
3.10 ksi
ASTM D412
Flexural Modulus 0.0896 GPa
13.0 ksi
ASTM D412
Tear Strength 105 kN/m
599 pli
ASTM D624
Taber Abrasion, mg/1000 Cycles 4.0
4.0
CS17 Wheel, 1000g; ASTM D1044
Compression Set 30 %

@Temperature 25.0 °C,
Time 79200 sec
30 %

@Temperature 77.0 °F,
Time 22.0 hour
ASTM D395, Method B
80 %

@Temperature 70.0 °C,
Time 79200 sec
80 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395, Method B
Tensile Set 60 %
60 %
Elongation set after break; ASTM D412
Thermal Properties Metric English Comments
CTE, linear 153 µm/m-°C

@Temperature 20.0 °C
85.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Vicat Softening Point 81.0 °C
178 °F
120°C/hr, 9.8N; ASTM D1525
Glass Transition Temp, Tg -15.0 °C
5.00 °F
DSC
Processing Properties Metric English Comments
Melt Temperature 182 - 199 °C
360 - 390 °F
Extrusion
Mold Temperature 16.0 - 60.0 °C
60.8 - 140 °F
Drying Temperature 88.0 - 104 °C
190 - 219 °F
air dew point <-40°C