- Lubrizol ESTALOC® 60155 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane
Lubrizol ESTALOC® 60155 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTALOC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol ESTALOC® 60155 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Fast Cycling, Dimensional Stability, Durability, Aesthetics, Low Temperature ImpactUses: Injection MoldingAvailability: Americas and AsiaInformation provided by Lubrizol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | flex bar; ASTM D955 |
| 0.0040 cm/cm | 0.0040 in/in | average flow and against flow, disc; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 - 69 @Time 5.00 sec |
63 - 69 @Time 0.00139 hour |
ASTM D2240 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Tensile Modulus | 0.552 GPa | 80.0 ksi | ASTM D638 |
| Flexural Strength | 19.0 MPa | 2760 psi | ASTM D790 |
| Flexural Modulus | 0.552 GPa | 80.0 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| 0.267 J/cm @Temperature -40.0 °C |
0.500 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.8 °C | 109 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 213 °C | 415 °F | |
| Middle Barrel Temperature | 218 °C | 424 °F | |
| Front Barrel Temperature | 218 °C | 424 °F | |
| Nozzle Temperature | 221 °C | 430 °F | |
| Melt Temperature | 221 °C | 430 °F | |
| Drying Temperature | 104 °C | 219 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Dew Point | -40.0 °C | -40.0 °F | |
| Injection Pressure | 69.0 - 103 MPa | 10000 - 14900 psi | |
| Hold Pressure | 35.0 - 69.0 MPa | 5080 - 10000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- Kolon KOPA® KN333HI4 High Impact Nylon 66
- LG Chemical Lupoy 1301V-10 Polycarbonate Resin
- MRC Polymers MAXTELâ„¢ 640-BK Polypropylene Copolymer
- KKPC KOSYN KNB 0230L Acrylonitrile Butadiene Rubber (NBR)
- Styron EMERGEâ„¢ 7500 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)
- SABIC Innovative Plastics Valox® IQNH4565 PBT (Asia Pacific)
- Westlake Hifor Xtreme SC74836 Linear Low Density Polyethylene
- Eurotec® Tecotek® PC30 NL VB03 PC, unfilled, UV stabilized, high impact, natural
- Weartech International NOREM 04B Iron Hardfacing & Wear Resistant Alloy
Copyright © lookpolymers.com All Rights Reserved