- Lubrizol Advanced Materials Pearlbond® D1160 Thermoplastic Polyurethane
Lubrizol Advanced Materials Pearlbond® D1160 Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlbond® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials Pearlbond® D1160 Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Pearlbondâ„¢ D1160 is a linear, aromatic polyurethane, supplied in form of small white granules, which combines a high crystallization rate and high thermoplasticity level. Applications: Pearlbondâ„¢ D1160 is used for obtaining PU films by extrusion (blown and cast) for solvent-free adhesion, by heat-seal process.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ISO 2781 |
| Brookfield Viscosity | 550 - 1500 cP | 550 - 1500 cP | 15% MEK; MQSA 40A |
| Melt Flow | 10 - 20 g/10 min @Load 5.00 kg, Temperature 190 °C |
10 - 20 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Storage Temperature | 15.0 - 25.0 °C | 59.0 - 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90.0 | 90.0 | ISO 2781 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | Extruded films: approx. 0.2 mm thickness; ISO 527 |
| Elongation at Break | 717 % | 717 % | Extruded films: approx. 0.2 mm thickness; ISO 527 |
| 100% Modulus | 0.00500 GPa | 0.725 ksi | Extruded films: approx. 0.2 mm thickness; ISO 527 |
| 300% Modulus | 0.00600 GPa | 0.870 ksi | Extruded films: approx. 0.2 mm thickness; ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 90.0 - 95.0 °C | 194 - 203 °F | MQSA 70 A |
| Softening Point | 80.0 - 85.0 °C | 176 - 185 °F | MQSA 70A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 115 - 125 °C | 239 - 257 °F | |
| Zone 2 | 200 - 210 °C | 392 - 410 °F | |
| Zone 3 | 200 - 210 °C | 392 - 410 °F | |
| Zone 4 | 170 - 180 °C | 338 - 356 °F | |
| Die Temperature | 170 - 180 °C | 338 - 356 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crystallization Rate | High | MQSA 12 B |
| Thermoplasticity | High | MQSA 68 A |
Users viewing this material also viewed the following:
- PolyChem Alloy FilmStat 3K2
- PolyOne Edgetek® XT XT-100-BW01 Natural PC+PBT (discontinued **)
- Kazanorgsintez Proxamine 385, 50%
- Mitsubishi Xantar® F 25 UR Polycarbonate
- SABIC Innovative Plastics ULTEM 2210R PEI (Asia Pacific)
- Styrolution Terlux® 2812 TR MABS
- CP-Polymer-Technik Wellamid® 6600 GS 40 HWCP 40% Glass Sphere Filled Nylon 66, Heat Stabilized, Conditioned
- Chosun Refractories CTC-85TD Monolithic Refractories for Ladle and Tundish
- Arlon 510-638R-50 0.008" (0.203 mm) Silicone Rubber Coated Fiberglass
- PolyOne Lubri-Tech™ MP-30GF/15T Modified PPO - 30% Glass Fiber - 15% PTFE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved