Lubrizol Advanced Materials PEARLTHANE® 11T98 Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlthane® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials PEARLTHANE® 11T98 Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PEARLTHANE® 11T98 is a polycaprolactone copolyester based TPU, supplied in form of translucent, colorless pellets, combining high hardness with excellent mechanical properties. It can be extruded and injection-molded. PEARLTHANE® 11T98 when extruded, is used for making tubing, profiles and a variety of technical parts. When processed by injection molding, can be used for making sport shoe soles (football, golf shoes), wheels, seals, etc.All information provided by Merquinsa
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg |
10 g/10 min @Load 47.6 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 98 | 98 | ASTM D2240 |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength, Yield | 40.1 MPa | 5810 psi | ASTM D412 |
| Elongation at Break | 470 % | 470 % | ASTM D412 |
| 100% Modulus | 0.01603 GPa | 2.325 ksi | ASTM D412 |
| 300% Modulus | 0.02906 GPa | 4.215 ksi | ASTM D412 |
| Tear Strength | 175 kN/m | 1000 pli | ASTM D624 (Die C) |
| Abrasion | 25 | 25 | loss (mm³); DIN 53.516 |
| Compression Set | 32 % @Temperature 22.8 °C, Time 252000 sec |
32 % @Temperature 73.0 °F, Time 70.0 hour |
ASTM D395 |
| 42 % @Temperature 70.0 °C, Time 86400 sec |
42 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 193 - 203 °C | 379 - 397 °F | MQSA 111 |
| Glass Transition Temp, Tg | -30.0 °C | -22.0 °F | DSC, 10ºC/min; DIN 51.007 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 196 °C | 385 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |
| Zone 1 | 170 - 200 °C | 338 - 392 °F | |
| Zone 2 | 180 - 210 °C | 356 - 410 °F | |
| Zone 3 | 190 - 215 °C | 374 - 419 °F | |
| Zone 4 | 200 - 220 °C | 392 - 428 °F | |
| Die Temperature | 215 - 220 °C | 419 - 428 °F | |
| Mold Temperature | 35.0 °C | 95.0 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | MQSA 44 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 205°C | |
| Metering Zone | 215°C |
Users viewing this material also viewed the following:
- Kolon ELLAS K-585A Caprolactone Based Thermoplastic Polyurethane
- LATI Latamid 12 H2 K/30 PA 12, 30% Carbon Fiber Reinforced, Heat Stabilized
- SABIC Innovative Plastics LNP LUBRICOMP UFL36SXC PPA
- SABIC Innovative Plastics Valox® V8090 PBT+PET (Europe-Africa-Middle East)
- Polyplastics Duranex® 531HS Polybutylene Terephthalate (PBT), Hydrolysis resistant, Heat shock resistant, Heat Shock Resistant
- China Tungsten YG4C Cemented Tungsten Carbide for Mining Purposes
- EMS-Griltech Grilon® TN 2200 White Nylon 6 Fiber
- 3M FM53R2 White Polyester Label Products
- Resinlab® EP1310 Medium Reactivity Epoxy Encapsulant
Copyright © lookpolymers.com All Rights Reserved