Hexcel® HexPly® 8552 Epoxy Matrix, SGP196-PW Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® HexPly® 8552 Epoxy Matrix, SGP196-PW Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 391 MPa
<br>@Temperature 25.0 °C
 56700 psi
<br>@Temperature 77.0 °F
 Open Hole Tensile, Dry
862 MPa
<br>@Temperature -55.0 °C
 125000 psi
<br>@Temperature -67.0 °F
 90°, Dry
945 MPa
<br>@Temperature 25.0 °C
 137000 psi
<br>@Temperature 77.0 °F
 90°, Dry
979 MPa
<br>@Temperature -55.0 °C
 142000 psi
<br>@Temperature -67.0 °F
 0°, Dry
979 MPa
<br>@Temperature 104 °C
 142000 psi
<br>@Temperature 220 °F
 90°, Dry
1090 MPa
<br>@Temperature 25.0 °C
 158000 psi
<br>@Temperature 77.0 °F
 0°, Dry
Tensile Modulus 79.3 GPa
<br>@Temperature 220 °C
 11500 ksi
<br>@Temperature 428 °F
 90°, Dry
80.0 GPa
<br>@Temperature -67.0 °C
 11600 ksi
<br>@Temperature -88.6 °F
 90°, Dry
80.0 GPa
<br>@Temperature 77.0 °C
 11600 ksi
<br>@Temperature 171 °F
 90°, Dry
84.8 GPa
<br>@Temperature -67.0 °C
 12300 ksi
<br>@Temperature -88.6 °F
 0°, Dry
84.8 GPa
<br>@Temperature 77.0 °C
 12300 ksi
<br>@Temperature 171 °F
 0°, Dry
Flexural Yield Strength 1140 MPa
<br>@Temperature 25.0 °C
 165000 psi
<br>@Temperature 77.0 °F
 0°, Dry
Flexural Modulus 76.5 GPa
<br>@Temperature 25.0 °C
 11100 ksi
<br>@Temperature 77.0 °F
 0°, Dry
Compressive Yield Strength 293 MPa
<br>@Temperature 25.0 °C
 42500 psi
<br>@Temperature 77.0 °F
 Compression After Impact, Dry
359 MPa
<br>@Temperature 25.6 °C
 52100 psi
<br>@Temperature 78.0 °F
 Open Hole Compression, Dry
558 MPa
<br>@Temperature 82.2 °C
 81000 psi
<br>@Temperature 180 °F
 0°, Wet, Fill Compression
600 MPa
<br>@Temperature 104 °C
 87000 psi
<br>@Temperature 220 °F
 0°, Wet, Fill Compression
655 MPa
<br>@Temperature 104 °C
 95000 psi
<br>@Temperature 220 °F
 0°, Wet, Fill Compression
710 MPa
<br>@Temperature 104 °C
 103000 psi
<br>@Temperature 220 °F
 0°, Dry, Fill Compression
800 MPa
<br>@Temperature 25.0 °C
 116000 psi
<br>@Temperature 77.0 °F
 0°, Dry, Fill Compression
855 MPa
<br>@Temperature -55.0 °C
 124000 psi
<br>@Temperature -67.0 °F
 0°, Dry, Fill Compression
Shear Strength 60.7 MPa
<br>@Temperature 82.2 °C
 8800 psi
<br>@Temperature 180 °F
 0° Short Beam, Wet
68.9 MPa
<br>@Temperature 104 °C
 10000 psi
<br>@Temperature 220 °F
 0° Short Beam, Dry
80.0 MPa
<br>@Temperature 25.0 °C
 11600 psi
<br>@Temperature 77.0 °F
 0° Short Beam, Wet
87.6 MPa
<br>@Temperature 25.0 °C
 12700 psi
<br>@Temperature 77.0 °F
 0° Short Beam, Dry
107 MPa
<br>@Temperature 104 °C
 15500 psi
<br>@Temperature 220 °F
 +/- 45° In-Plane, Dry
126 MPa
<br>@Temperature 25.0 °C
 18300 psi
<br>@Temperature 77.0 °F
 +/- 45° In-Plane, Dry
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Epoxy Matrix Limit