Lord Adhesives Aeroglaze® Z307 Absorptive Conductive Polyurethane
| Category | Polymer , Thermoset , Polyurethane, TS |
| Manufacturer | Lord Adhesives |
| Trade Name | Aeroglaze® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Aeroglaze® Z307 Absorptive Conductive Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aeroglaze® Z307 black absorptive conductive polyurethane coating is primarily for application to substrates used on spacecraft. These applications include those where coatings must exhibit low outgassing characteristics while providing static dissipating and high thermal absorptivity properties.In addition, the mechanical properties required for rigorous durations in space are an integral part of the Aeroglaze Z307 coating make-up. Aeroglaze Z307 coating shows excellent performance on rigid or flexible substrates.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.870 g/cc | 0.0314 lb/in³ | ASTM D1475-85 |
| Solids Content | 18 % | 18 % | by volume |
| 22 % | 22 % | by weight | |
| Volatile Organic Compounds (VOC) Content | 728 g/l | 728 g/l | ASTM D3960-89 |
| Brookfield Viscosity | 300 cP @Temperature 25.0 °C |
300 cP @Temperature 77.0 °F |
ASTM D2196-86; LVT |
| Outgassing - Total Mass Loss | 1.06 % | 1.06 % | 40 day cure at room temperature |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flash Point | 19.3 °C | 66.7 °F | Setaflash, Closed Cup; ASTM D3278-82 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | <= 15 % | <= 15 % | 60° |
| Emissivity (0-1) | 0.89 | 0.89 | ASTM E408-71 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ohms/in² @ .75-1.5 mils |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 180 min @Temperature 25.0 °C |
2.00 - 3.00 hour @Temperature 77.0 °F |
Tack Free; 50% relative humidity |
| 720 min @Temperature 25.0 °C |
12.0 hour @Temperature 77.0 °F |
Permit Handling | |
| 2160 - 2880 min @Temperature 25.0 °C |
36.0 - 48.0 hour @Temperature 77.0 °F |
Permit Normal Usage | |
| Shelf Life | 12.0 Month | 12.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Flat Black | |
| Coating Film Dry Weight (gm/ft²/mil) | 2.69 | |
| Solar Absorption | 0.97 | Gier-Dunkle Integrating Sphere |
| Theoretical Coverage (ft²/gallon/mil) | 284 |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_9895/9795 Rubber-like Prototyping Polymer
- Nitriflex N-608 NBR - Nitrile Rubber
- Microcell Composite Company CELLOMER® 6000 SBS Rubber Pellets
- Huntsman AVALON® 92 AE Thermoplastic Polyurethane
- ExxonMobil Diol 13 RD 40
- UBE UBESTA® 3030U Nylon 12 (After Fuel C/E10 for 500 hours)
- EMS-Griltech Grilon® KA 140 White CoPA Fiber
- EMS-Grivory Grivory® BM 17 PA*
- Fainplast Compounds PM 5740 Flexible PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved