- Lehmann & Voss LUVOCOM® 1850-8282 PBT, with carbon fiber
Lehmann & Voss LUVOCOM® 1850-8282 PBT, with carbon fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1850-8282 PBT, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricity.Strong, stiff parts.Resistant to aliphatic hydrocarbon, oil, grease, dilute acid and alkali, cleaning solvent and salt solution.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 130 MPa | 18900 psi | |
| Elongation at Yield | 1.8 % | 1.8 % | |
| 2.3 % | 2.3 % | flexural | |
| Modulus of Elasticity | 16.0 GPa | 2320 ksi | |
| Flexural Strength | 190 MPa | 27600 psi | |
| Flexural Modulus | 14.0 GPa | 2030 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 180 °C | 356 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | |
| Zone 1 | 240 - 260 °C | 464 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec |
176 °F @Time 6.00 - 8.00 hour |
Vacuum Dryer |
| 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Less Common Metals Yttrium Vacuum Remelted Rare Earth Metal
- MarkeTech Repton EXP 93 Cordierite Mullite
- Polyram Polytron A60B02 Nylon 66, Chemically Coupled 60% Long Fiber
- Polyram RamOfin PPH308G50 Polypropylene, 50% Glass Fiber, Impact Modified
- Chosun Refractories SB75 Bricks, Oxide Bonded SiC
- E-Polymers TEKAMID® TB120G15T Impact Modified, 15% Glass Fiber Reinforced PA6, DAM
- ConocoPhillips Hydroclear® El Mar® Ashless Heavy Duty SAE 30
- Cheng Yu Plastic FRCV200 Flame Retardant Nylon 66, 30% Mineral Reinforced
- Bapolene® 4082NA Polypropylene
- SABIC Innovative Plastics GELOY CR7500 ASA
Copyright © lookpolymers.com All Rights Reserved