Lehmann & Voss LUVOCOM® 1106-7033 Polyether imide, with carbon fiber
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1106-7033 Polyether imide, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: High-strength and high-stiff parts; low coefficient of expansion.High continuous use and heat distortion temperature. Non flammable.High dimensionally stable precision parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 200 MPa | 29000 psi | |
| Elongation at Yield | 1.0 % | 1.0 % | |
| 1.3 % | 1.3 % | flexural | |
| Modulus of Elasticity | 25.0 GPa | 3630 ksi | |
| Flexural Strength | 300 MPa | 43500 psi | |
| Flexural Modulus | 21.0 GPa | 3050 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |
| Insulation Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 380 °C | 716 °F | mass temp |
| Nozzle Temperature | 350 - 400 °C | 662 - 752 °F | |
| Zone 1 | 330 - 350 °C | 626 - 662 °F | |
| Zone 2 | 340 - 390 °C | 644 - 734 °F | |
| Zone 3 | 350 - 400 °C | 662 - 752 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 120 °C @Time >=28800 sec |
248 °F @Time >=8.00 hour |
Dehumidifying dryer |
| 150 °C @Time >=14400 sec |
302 °F @Time >=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Nye Lubricants 188B (SO) Synthetic Oil
- Potters Industries A-Series Premium 2MM Soda-Lime Silica Technical Quality Solid Glass Spheres
- Gouda Vuurvast FI 25-15 Insulating Refractory Brick
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N990 Filler
- DuPont Performance Polymers Hytrel® G4078LS NC010 Polyester Elastomer TPC-ET (Unverified Data**)
- 3M CC-3 Cleaning Pad Kits
- A. Schulman LP544-01 High-Density Copolymer Polyethylene
- Solvay Specialty Polymers Amodel® A-6135 NL Polyphthalamide (PPA), 35% Glass Fiber Reinforcement (discontin
- DuPont Performance Polymers Zytel® RS 3261THSL BK041A Nylon 610 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved