- Lehmann & Voss LUVOCOM® 1105-8179 PEEK, with carbon fiber
Lehmann & Voss LUVOCOM® 1105-8179 PEEK, with carbon fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-8179 PEEK, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 280 MPa | 40600 psi | |
| Elongation at Yield | 1.3 % | 1.3 % | |
| 1.7 % | 1.7 % | flexural | |
| Modulus of Elasticity | 34.0 GPa | 4930 ksi | |
| Flexural Strength | 405 MPa | 58700 psi | |
| Flexural Modulus | 27.0 GPa | 3920 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 300 °C | 572 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 330 °C | 626 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EMB405L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Nye Lubricants 227(SO) Synthetic Oil
- RheTech Products HP521-229 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 195A Medium Neutral
- Abatron AboCast 8-16/Abocure 8-16 Epoxy (discontinued **)
- Indium Corp. Indalloy 281-338 Bismuth-Tin Solder Alloy
- Samsung Cheil Industries Infino® NH-1017D PC/ABS, Unreinforced FR
- SABIC Innovative Plastics LNP THERMOCOMP WH0270F PBT
- Eastman PROVISTA Copolymer PETG Copolyester
- Clariant Renol PA211G13 Nylon 6, 13% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved