- Lehmann & Voss LUVOCOM® 1100-7890 Polyether sulfone, with carbon fiber
Lehmann & Voss LUVOCOM® 1100-7890 Polyether sulfone, with carbon fiber
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone, Carbon Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1100-7890 Polyether sulfone, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Especially suitable for thin wall complex parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Superheated steam sterilizable.High quality terminal bar, switches and plugs, relais, lamp reflectors, sterilizable medical equipment.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 130 MPa | 18900 psi | |
| Elongation at Yield | 2.1 % | 2.1 % | |
| 2.8 % | 2.8 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 190 MPa | 27600 psi | |
| Flexural Modulus | 9.00 GPa | 1310 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| 200 °C | 392 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 340 - 360 °C | 644 - 680 °F | |
| Zone 1 | 355 - 375 °C | 671 - 707 °F | |
| Zone 2 | 360 - 380 °C | 680 - 716 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 200 °C | 248 - 392 °F | |
| Drying Temperature | 150 °C @Time 10800 - 18000 sec |
302 °F @Time 3.00 - 5.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Asahi Kasei Tenac®-C 4510 Acetal Copolymer, General Purpose (discontinued **)
- Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes
- Solvay Specialty Polymers Polidan® EC/MD Polyethylene, Crosslinked (XLPE)
- A. Schulman POLYBATCH™ Bright Pink 50379 Concentrate Based In Polyethylene
- Tra-Con Tra-Bond F123NC High Temperature Fiber Optic Epoxy Adhesive
- A. Schulman SCHULAMID® 66 MK4015 40% Glass Fiber/Mineral Reinforced 66
- Dow Corning SYL-OFF® SL 6 CROSSLINKER
- Covestro Makrolon® DP1-1825* Polycarbonate, Impact Grade
- Arlon 55578R036 0.036" (0.914 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Ashley Polymers Ashlene® 114WO PBT Polyester
Copyright © lookpolymers.com All Rights Reserved