Lanxess Pocan® DP T 7140 LDS 000000 PBT + PET, 44% Mineral + L227Glass Fiber  (discontinued **)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® DP T 7140 LDS 000000 PBT + PET, 44% Mineral + L227Glass Fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PET+PBT, 44% glass fibers/mineral, injection molding, LDS, high thermal dimension stability
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
ISO 1183
Viscosity Test 50 cm³/g
50 cm³/g
Viscosity number; ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow 0.0015 cm/cm
0.0015 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ISO 294-4, 2577
Melt Flow 32 g/10 min

@Load 2.16 kg,
Temperature 280 °C
 32 g/10 min

@Load 4.76 lb,
Temperature 536 °F
 Calculated from MVR using melt density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
ISO 527-1/-2
Elongation at Break 1.1 %
1.1 %
ISO 527-1/-2
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527-1/-2
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
3.00 J/cm²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 36.0 µm/m-°C
20.0 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 56.0 µm/m-°C
31.1 µin/in-°F
ISO 11359-1/-2
Melting Point 255 °C
491 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+20 ohm-cm
2.00e+20 ohm-cm
IEC 60093
Surface Resistance 5.40e+16 ohm
5.40e+16 ohm
IEC 60093
Dielectric Constant 4.1

@Frequency 1.00e+6 Hz
 4.1

@Frequency 1.00e+6 Hz
 IEC 60250
4.3

@Frequency 100 Hz
 4.3

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 33.0 kV/mm
838 kV/in
IEC 60243-1
Dissipation Factor 0.0022

@Frequency 100 Hz
 0.0022

@Frequency 100 Hz
 IEC 60250
0.0138

@Frequency 1.00e+6 Hz
 0.0138

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Form Pellets
ISO Shortname ISO7792-PET+PBT,GHMR,07-120,(GF+MD)44
Processing Injection molding