Lanxess Pocan® B 700 000000 PBT (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® B 700 000000 PBT
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, extrusion, improved flowability
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4, 2577 |
| Melt Flow | 236 g/10 min @Load 2.16 kg, Temperature 250 °C |
236 g/10 min @Load 4.76 lb, Temperature 482 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ISO 527-1/-2 |
| Elongation at Break | 2.9 % | 2.9 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 2.9 % | 2.9 % | ISO 527-1/-2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,G,05-030 | |
| Processing | Blow molding | |
| Injection molding | ||
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 105 PC
- Lehmann & Voss LUVOCOM® 80-7695 Polyacetal-copolymer, with glass fiber and PTFE
- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
- Polyplastics Duranex® 407EP Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance
- Trelleborg R798 Commercial Natural Rubber Polyisoprene
- Arlon 10502R020 0.020" (0.508 mm) Cured Silicone Rubber (Unsupported)
- Carmel Olefins CAPILENE® T 50 Polypropylene Homopolymer
- 3M FV053 Tire Vinyl Label Products
- Bhansali Engineering Abstron IM-14G ABS Very High Rigidity Injection Molding Grade
- Borealis Bormed™ HE7541-PH HDPE for Healthcare Applications
Copyright © lookpolymers.com All Rights Reserved