Lanxess Pocan® B 3217 XF 000000 PBT, 16% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® B 3217 XF 000000 PBT, 16% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 16% glass fibers, injection molding, improved flowability, impact modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0011 cm/cm | 0.0011 in/in | ISO 294-4, 2577 |
| Melt Flow | 55 g/10 min @Load 2.16 kg, Temperature 260 °C |
55 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527-1/-2 |
| Elongation at Break | 3.2 % | 3.2 % | ISO 527-1/-2 |
| Tensile Modulus | 6.10 GPa | 885 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GHMPR,07-060,GF16 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY HRA222F ASA+PC (Europe-Africa-Middle East)
- NIZHNEKAMSKNEFTEKHIM PE 2062U (62111) High Density Polyethylene
- LATI LAESTRA E01 G/30 30% Glass Fiber Reinforced, Elastomer Modified Syndiotactic Polystyrene (SPS) (disconti
- Unifrax Fiberfrax® Round Braid
- Zhejiang Juner 301-G10 10% Glass Fibre Reinforced and Flammable Resistant
- Zotefoams Plastazote® LD30SD Static Dissipative Low Density Polyethylene Foam
- A. Schulman POLYBATCH™ Green 3015 Concentrate Based In Polyethylene
- Ensinger Tecatron® XP-76 Compression Molded PPS Compound, 55% PTFE Filled Seal Material
- Assab Steels HOTVAR Hot Work Steel
Copyright © lookpolymers.com All Rights Reserved