Lanxess Durethan® BKV 30 H2.0 EF 900116 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 30 H2.0 EF 900116 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Melt Flow | 101 g/10 min @Load 5.00 kg, Temperature 270 °C |
101 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
| 170 MPa | 24700 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.2 % | 3.2 % | ISO 527-1/-2 |
| 5.8 % | 5.8 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 5.50 GPa | 798 ksi | Conditioned; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 803 | 803 | Puncture maximum force (N); ISO 6603-2 |
| 744 @Temperature -30.0 °C |
744 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.60 J | 1.92 ft-lb | ISO 6603-2 |
| 2.60 J @Temperature -30.0 °C |
1.92 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.60 J @Temperature -30.0 °C |
1.92 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 150 °C | 302 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| ISO Shortname | ISO1874-PA6, MHR, 10-090, GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Quadrant EPP TIVAR® Dockguard - UHMW-PE - Black UV Stabilized UHMW-PE (ASTM Product Data Sheet)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Suprex Clay Filler
- Gwent Electronic Materials C2040308D2 Silver/Silver Chloride Paste
- Saint-Gobain CHR® M746 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- Cheng Yu Plastic N6G20 Nylon 6, 20% Glass Filled
- Dow Corning FOX® PMCP12 Flowable Oxide
- ExxonMobil Escorene™ MV 02514 Ethylene Vinyl Acetate Copolymer (European Grade)
- 3M AC-236 Class B-1/2 Aerospace Sealant
- Chem Polymer Chemlon 223 Nylon 6, Nucleated
- Indium Corp. 99.999% InF3 Indium Trifluoride, Anhydrous
Copyright © lookpolymers.com All Rights Reserved