LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: High Impact ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
Method A; ASTM D792
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
ASTM D638
Tensile Strength, Yield 140 MPa
20300 psi
ASTM D638
Elongation at Break 3.4 %
3.4 %
ASTM D638
Elongation at Yield 3.3 %
3.3 %
ASTM D638
Tensile Modulus 8.48 GPa
1230 ksi
ASTM D638
Flexural Strength 207 MPa
30000 psi
ASTM D790
Flexural Modulus 7.03 GPa
1020 ksi
ASTM D790
Izod Impact, Notched 1.28 J/cm

@Thickness 3.18 mm
2.40 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 11.6 J/cm

@Thickness 3.18 mm
21.7 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 15.4 kJ/m²
7.33 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 73.4 kJ/m²
34.9 ft-lb/in²
ISO 180
Falling Dart Impact 9.30 J
6.86 ft-lb
ASTM D3763
Impact Test 3.52 J
2.60 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 31.0 µm/m-°C

@Temperature 20.0 °C
17.2 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 88.0 µm/m-°C

@Temperature 20.0 °C
48.9 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi) 208 °C
406 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 268 - 274 °C
514 - 525 °F
Mold Temperature 82.2 - 93.3 °C
180 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi