LNP Lubricomp® OFL-4536 Polyphenylene Sulfide, Glass Fiber Reinforced, PTFE Lubricant (discontinued **)

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LNP Lubricomp® OFL-4536 Polyphenylene Sulfide, Glass Fiber Reinforced, PTFE Lubricant (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Physical Properties	Metric	English	Comments
Specific Gravity	1.65 g/cc	1.65 g/cc	Method A; ASTM D792
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	109 MPa	15800 psi	ASTM D638
Elongation at Break	1.7 %	1.7 %	ASTM D638
Flexural Strength	152 MPa	22000 psi	ASTM D790
Flexural Modulus	11.4 GPa	1650 ksi	ASTM D790
Izod Impact, Notched	0.587 J/cm @Thickness 3.18 mm	1.10 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	3.47 J/cm @Thickness 3.18 mm	6.50 ft-lb/in @Thickness 0.125 in	ASTM D256
Coefficient of Friction, Dynamic	0.41	0.41	vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static	0.38	0.38	vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor	103 x 10^-8 mm³/N-M	51.0 x 10^-10 in³-min/ft-lb-hr	40psi, 50ft/min; tested in accordance with LNP WI-0687

Processing Properties	Metric	English
Melt Temperature	316 - 321 °C	601 - 610 °F
Mold Temperature	135 - 163 °C	275 - 325 °F
Drying Temperature	121 - 149 °C	250 - 300 °F
Dry Time	4 hour	4 hour
Back Pressure	0.172 - 0.345 MPa	24.9 - 50.0 psi

Users viewing this material also viewed the following: