LG Chemical SEETEC PF150 HDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | LG Chemical |
| Trade Name | SEETEC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SEETEC PF150 HDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Characteristics: Good impact & tear strength, High speed & superior heat sealing propertiesAdditives: Anti-oxidants, LubricantsApplication: Shopping bags, Thin films, Trash bags, Multiwall bag liners, PolyglovesCAS No. 25213-02-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.944 - 0.947 g/cc | 0.944 - 0.947 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50; ASTM D1693 |
| Melt Flow | 0.15 - 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 - 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 55 | 55 | ASTM D785 |
| Tensile Strength, Yield | 17.7 MPa | 2560 psi | 50 mm/min; ASTM D638 |
| Film Elongation at Break, MD | 500 % @Thickness 0.0250 mm |
500 % @Thickness 0.000984 in |
ASTM D882 |
| Film Elongation at Break, TD | 650 % @Thickness 0.0250 mm |
650 % @Thickness 0.000984 in |
ASTM D882 |
| Elongation at Break | >= 500 % @Thickness 50.0 mm |
>= 500 % @Thickness 1.97 in |
ASTM D638 |
| Flexural Modulus | 1.18 GPa | 171 ksi | ASTM D790 |
| Elmendorf Tear Strength MD | 20 g @Thickness 0.0250 mm |
20 g @Thickness 0.000984 in |
ASTM D1922 |
| Elmendorf Tear Strength TD | 200 g @Thickness 0.0250 mm |
200 g @Thickness 0.000984 in |
ASTM D1922 |
| Dart Drop Test | 120 g | 0.265 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 47.1 MPa @Thickness 0.0250 mm |
6830 psi @Thickness 0.000984 in |
ASTM D882 |
| Film Tensile Strength at Break, TD | 55.9 MPa @Thickness 0.0250 mm |
8110 psi @Thickness 0.000984 in |
ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 135 °C | 275 °F | 10°C/min; ASTM D3418 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- Polimeri Europa Intol® 1739 Emulsion Styrene-Butadiene Rubber
- Global GPC-110 10% Glass Reinforced Polycarbonate
- Lord Adhesives Thermosetâ„¢ LS 213-9 Unfilled Epoxy Encapsulant
- Lucobit Lucofin® 1400HN Powder Ethylene Butyl Acrylate
- Techmer ES Elastoblend® PA6/66 IM 6040 MB
- A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene
- CRP Technology AMC225xe Aluminum Alloy - SiC Composite, T4 Condition
- ExxonMobil LLDPE LL 3003.39 Linear Low Density Polyethylene Resin
- Clariant Renol PA143G10 Nylon 6/66 Copolymer, 10% Glass Fiber, Heat Stabilized
- Asahi Kasei Xyron® 140Z Modified Polyphenylene Ether