- LG Chemical NBR 6250 High Acrylonitrile Polymer
LG Chemical NBR 6250 High Acrylonitrile Polymer
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical NBR 6250 High Acrylonitrile Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: NBR 6250 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6250 is a non staining, medium mooney, and medium high acrylonitrile polymer designed to aid in processing operations such as extruding and calendaring. NBR 6250 is a low temperature polymerized polymer, and such as, retains the excellent physical and processing properties of a cold nitrile rubber. NBR 6250 is a high mooney version of NBR 6240. Applications: NBR 6250 is recommended to use in packings, shoe products, chemically blown sponge, oil field products, industrial and automotive molded parts.CAS No: 9003-18-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | |
| Volatiles | 0.20 % | 0.20 % | |
| Mooney Viscosity | 50 @Temperature 100 °C |
50 @Temperature 212 °F |
ML 1+4 |
| Ash | <= 0.50 % | <= 0.50 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 @Temperature 145 °C, Time 1190 sec |
69 @Temperature 293 °F, Time 0.330 hour |
Cured |
| 70 @Temperature 100 °C, Time 259000 sec |
70 @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging | |
| 45 @Treatment Temp. 25.0 °C, Time 259000 sec |
45 @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 68 @Treatment Temp. 100 °C, Time 259000 sec |
68 @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| 70 @Treatment Temp. 100 °C, Time 259000 sec |
70 @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| Tensile Strength at Break | 19.1 MPa @Temperature 145 °C, Time 1190 sec |
2770 psi @Temperature 293 °F, Time 0.330 hour |
Cured |
| 19.9 MPa @Temperature 100 °C, Time 259000 sec |
2890 psi @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging | |
| 28.7 MPa @Temperature 145 °C, Time 2990 sec |
4160 psi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 | |
| 14.1 MPa @Treatment Temp. 25.0 °C, Time 259000 sec |
2050 psi @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 19.6 MPa @Treatment Temp. 100 °C, Time 259000 sec |
2840 psi @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| 19.6 MPa @Treatment Temp. 100 °C, Time 259000 sec |
2840 psi @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| Elongation at Break | 392.6 % @Temperature 100 °C, Time 259000 sec |
392.6 % @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging |
| 410 % @Temperature 145 °C, Time 1190 sec |
410 % @Temperature 293 °F, Time 0.330 hour |
Cured | |
| 558 % @Temperature 145 °C, Time 2990 sec |
558 % @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 | |
| 358.8 % @Treatment Temp. 25.0 °C, Time 259000 sec |
358.8 % @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 390.4 % @Treatment Temp. 100 °C, Time 259000 sec |
390.4 % @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| 392.4 % @Treatment Temp. 100 °C, Time 259000 sec |
392.4 % @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| 300% Modulus | 0.0128 GPa @Temperature 145 °C, Time 2990 sec |
1.86 ksi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 |
| Rebound | 46 % @Temperature 30.0 °C |
46 % @Temperature 86.0 °F |
|
| Abrasion | 0.3105 | 0.3105 | AKRON |
| Compression Set | 18.3 % @Temperature 100 °C, Time 259000 sec |
18.3 % @Temperature 212 °F, Time 72.0 hour |
160°C x 30 min. Cured) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Bound AN Content | 0.339 | |
| Color | Tan | |
| Components | HAF (IRB#7) | 40 phr, ASTM D3187 |
| NBR 6250 | 100 phr, ASTM D3187 | |
| Stearic Acid | 1 phr, ASTM D3187 | |
| Sulfur | 1.5 phr, ASTM D3187 | |
| TBBS | 0.7 phr, ASTM D3187 | |
| ZnO | 3 phr, ASTM D3187 | |
| Compound Recipe | Antioxidant(3-C) | 1 phr |
| Antioxidant(RD) | 2 phr | |
| Carbon Black(SRF) | 80 phr | |
| CZ | 2 phr | |
| NBR 6250 | 100 phr | |
| Plasticizer(DOP) | 10 phr | |
| Stearic Acid | 1 phr | |
| Sulfur | 0.5 phr | |
| TT | 1 phr | |
| Zinc Oxide | 5 phr | |
| Rheometer | 1.0 min | ts1, 160°C x 12 min, 1° Arc, MDR |
| 1.7 min | t'50, 160°C x 12 min, 1° Arc, MDR | |
| 2.0 lb-in | ML, 160°C x 12 min, 1° Arc, MDR | |
| 2.5 min | t'90, 160°C x 12 min, 1° Arc, MDR | |
| 25.0 lb-in | MH, 160°C x 12 min, 1° Arc, MDR | |
| Volume Swell | -0.017 | Aged ASTM D #3 Oil (100°C x 72hrs) |
| -0.062 | Aged ASTM D #1 Oil (100°C x 72hrs) | |
| 0.435 | Aged fuel C (RT°C x 72hrs) |
Users viewing this material also viewed the following:
- Shakespeare WP-500 diameter 0.5 mm Hydrolytically Stabilized Polyester Yarn
- Saint-Gobain Chemfab® 3 Tear Resistant PTFE-Coated Glass
- Techmer ES Electrablend® PA6 CF30 TL10 30% Carbon Filled
- A. Schulman SCHULADUR® A GF33HI 33% Glass Fiber Reinforced, High Impact PBT
- ChevronTexaco Pinnacle® EP 320
- EMS-Grivory Grivory® L 20 GM PA12
- AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, High Strength Low Alloy Steel (HSLA), 045XLK
- Techmer ES Plastiblend® ABS/PA 1700
- DuPont Performance Polymers Neoprene 671A Polychloroprene (discontinued **)
- H.C. Starck Amperit® 552.072 Tungsten Carbide - Chromium Carbide-Nickel 73-20-7 (WC-CrC-Ni)